| STICK(SMAW)堆焊手工焊條 |  
| 
 產(chǎn)品  | 
 直徑(mm)  | 
 成份  | 
 強度KSI  | 
 硬度 HRC  |  
| 
 19  | 
 3.2/4.0/4.8/6.4  | 
 26.0%C Mn Si Cr Mo  | 
  | 
 錳鋼二層45-49 中碳鋼二層51-55  |  
| 
 31  | 
  3.2/4.0/4.8/6.4
 
  | 
 34.0%C Mn Si Cr Mo  | 
  | 
 錳鋼二層47-49 碳鋼二層45-48  |  
| 
 35  | 
 3.2/4.0/4.8/6.4  | 
 38.0%C Mn Si Cr   | 
  | 
 錳鋼二層50-53 加硬達到58-60  |  
| 
 45  | 
 4.0  | 
 48.0%C Mn Si Cr Mo V Ti  | 
  | 
 59-61  |  
| 
 77  | 
 3.2/4.0/4.8/6.4  | 
 24.0%C Mn Si Cr Mo  | 
  | 
 錳鋼二層42-50 碳鋼二層49-54  |  
| 
 1102  | 
 3.2/4.0  | 
 10.7%C Mn Si Cr Ni  | 
  | 
 52-68  |  
| 
 1105  | 
 3.2/4.0/4.8/6.4  | 
 5.00%C Mn Si Cr Mo V  | 
    | 
 1045鋼二層38-42  |  
| 
 2110  | 
 3.2/4.0/4.8/6.4  | 
 31.0%C Mn Si Cr Ni  | 
  T.S.119 Y.S.76.4 EL40%  | 
 錳鋼二層 加硬達到50-55  |  
| 
 2134  | 
 4.0/4.8/6.4  | 
 36.0%C Mn Si Cr Mo  | 
    | 
 錳鋼二層45-50 1045板二層56-60  |  
| 
 BUILD UP LH  | 
 3.2/4.0/4.8/6.4  | 
 4.50%C Mn Si Cr Mo  | 
 T.S.118 Y.S.113 EL6%  | 
 中碳鋼一層27 中碳鋼三層31  |  
| 
  DYNAMANG
 
  | 
 3.2/4.0/4.8/6.4/8.0  | 
 21.0%C Mn Si Cr Ni  | 
 T.S.l20 Y.S.70 EL42%  | 
 錳鋼一層180BHN 加硬達到500BHN  |  
| 
 RAILEND932  | 
 4.0/4.8/6.4  | 
 6.00%C Mn Si Cr Mo  | 
 T.S.150  | 
 38-40  |  
| 
 SELF HARDENING  | 
 3.2/4.0/4.8/6.4  | 
 12.0%C Mn Si Cr Ni  | 
    | 
 52-58  |  
| 
 SUPERCHROME  | 
 3.2/4.0/4.8/6.4  | 
 38.0%C Mn Si Cr  | 
    | 
 錳鋼二層54-61 碳鋼二層58-63  |    |