| Sub堆焊埋弧焊絲 |  
| 
 產(chǎn)品  | 
 直徑(mm)  | 
 成份  | 
 焊劑  | 
 硬度 HRC  |  
| 
 103  | 
 3.2  | 
  36.0%C Mn Si Cr Zr  | 
 STOODY S  | 
  1040鋼二層54
 
  |  
| 
 104  | 
 2.8/3.2/4.0  | 
  6.00%C Mn Si Cr   | 
 STOODY S  | 
 碳鋼多層29  |  
| 
 105  | 
 3.2/4.0  | 
  7.00%C Mn Si Cr Mo V  | 
 STOODY S  | 
 1040鋼二層45  |  
| 
 105B  | 
 3.2/4.0  | 
  6.00%C Mn Si Cr Mo V  | 
 STOODY S  | 
 1040鋼二層43  |  
| 
 107  | 
 3.2/4.0  | 
  6.00%C Mn Si Cr Mo   | 
 STOODY S  | 
 1040鋼二層38  |  
| 
 410-S  | 
 2.8/3.2  | 
  14.0%C Mn Si Cr Mo Ni  | 
 L-880  | 
 T.S.75KSI EL25%  |  
| 
 410Ni Mo  | 
 2.8/3.2  | 
  18.0%C Mn Si Cr Mo Ni  | 
 L-50  | 
 T.S.116KSI EL25%  |  
| 
 420  | 
 3.2  | 
  23.0%C Mn Si Cr   | 
 L-880  | 
 42-48  |  
| 
 4552  | 
 3.2  | 
  12.0%C Mn Si Cr   | 
 STOODY S  | 
 1040鋼二層48  |  
| 
 CASTWELD NI55-S  | 
 2.4  | 
  55.0%Ni  | 
 STOODY R-20   | 
    |  
| 
 THERMACLAD 102  | 
    | 
  11.0%C Mn Si Cr Mo W  | 
 R-20/Thermaflux B  | 
 51  |  
| 
 THERMACLAD 423  | 
    | 
  19.3%C Mn Si Cr Mo V Ni Cb  | 
 R-20/Thermaflux B   | 
 47  |  
| 
 THERMACLAD 440  | 
    | 
  19.8%C Mn Si Cr Mo Ni   | 
 R-20/Thermaflux B   | 
 40  |  
| 
  THERMACLAD 4552
 
  | 
    | 
  16.9%C Mn Si Cr  | 
 R-20/Thermaflux B   | 
 53  |    |